裴广玉,李东,李凯斌,刘东宇.表面纳米化对纯铜扩散焊接性能的影响[J].轻工机械,2015,33(4): |
表面纳米化对纯铜扩散焊接性能的影响 |
Performance of Copper Diffusion Welding after Surface Nano-Crystallization |
|
DOI:I0. 3969/j . issn. 1005 -2895. 2015. 04. 010 |
中文关键词: 纯铜 扩散焊接 表面机械滚压 表面纳米化 |
英文关键词:fine copper diffusion welding Surface Mechanical Rolling Treatment( SMRT ) surface nano-crystallization |
基金项目:上海市自然科学基金(IIZR1414600);上海市教委创新项目(IIY2214) |
|
摘要点击次数: 1303 |
全文下载次数: 1327 |
中文摘要: |
为了提高纯铜扩散焊接性能,通过表面机械滚压技术( SMRT),对纯铜试样进行表面纳米化处理,并在真空下对
纯铜母材和经表面机械滚压处理的纯铜试样分别进行扩散焊接试验,焊接压力10 MPa,保温l h,焊接温度为300℃、
400℃、500 qC。研究结果表明:经过SMRT纯铜表层晶粒达到纳米级别,纯铜试样焊接接头处的显微硬度高于母材试
样;同一温度下,SMRT铜焊接性能优于母材试样。 |
英文摘要: |
To improve the diffusion welding properties of fine copper, the experiment was carried out on fine copper after
surface nano-crystallization treatment with Surface Mechanical Rolling Technology (SMRT) . And the tests of fine copper
base metal and copper samples treated by SMR were conducted in the vacuum. with welding pressure of 10 MPa. heat
preservation of I h and soldering temperature of 300 0C . 400 0C . 500 0C respectively. The results show that the surface
layer crystal grain of fine copper after SMRT reaches the nano level. and the micro-hardness of welded joints is higher
than the base metal samples. Under the same temperature. the diffusion welding properties of SMRT copper is
significantly improved. |